In this work we describe the synthesis and characterization of chalcogenide glass (0.3La2S3-0.7Ga2S 3) with low phonons frequencies. Several properties were measured like Sellmeier parameters, linear refractive index dispersion and material dispersion. Samples with the composition above were doped with Dy2S3. The absorption and emission characteristics were measured by electronic spectroscopy and fluorescence spectrum respectively. Raman and infrared spectroscopy shows that these glasses present low phonons frequencies and strucuture composed by GaS4 tetrahedrals. The Lines model was used for calculate the coefficients values of the non linear refractive index.

We describe the preparation and some optical properties of high refractive index TeO2-PbO-TiO2 glass system. Highly homogeneous glasses were obtained by agitating the mixture during the melting process in an alumina crucible. The characterization was done by X-ray diffraction, Raman scattering, light absorption and linear refractive index measurements. The results show a change in the glass structure as the PbO content increases: the TeO4 trigonal bipyramids characteristics of TeO2 glasses transform into TeO3 trigonal pyramids. However, the measured refractive indices are almost independent of the glass composition. We show that third-order nonlinear optical susceptibilities calculated from the measured refractive indices using Lines' theoretical model are also independent of the glass composition.